噴砂用白剛玉砂選用充分冶煉結晶的白剛玉固定爐料，經(jīng)過破碎、篩分等工藝生產(chǎn)而來。噴砂用白剛玉的粒徑范圍經(jīng)過嚴格控制，使磨粒大小控制在一定范圍內(nèi)。噴砂后產(chǎn)生表面一致的粗糙度。白剛玉韌性好，研磨能力強，自銳性好，噴射到噴砂工件表面時，通過氣流的沖擊力，工件撞擊出凹痕。鈍化后的噴砂表面有利于后續(xù)噴漆的油漆保持把持力。白剛玉噴砂磨粒還具有噴砂效率高，利用率高的優(yōu)點。

 The white fused aluminum oxide used for sandblasting is produced by using fully melted and crystallized white corundum as fixed furnace material, and is processed through processes such as crushing and screening. The particle size range of white corundum used for sandblasting is strictly coolled to keep the abrasive particle size within a certain range. After sandblasting, a consistent surface roughness is produced. White corundum has good toughness, strong grinding ability, and good self sharpening. When sprayed onto the surface of sandblasted workpieces, the impact force of the airflow causes the workpieces to produce dents. The sandblasted surface after passivation is beneficial for maintaining the grip of subsequent paint spraying. White corundum sandblasting abrasive particles also have the advantages of high sandblasting efficiency and high utilization rate.

白剛玉的特性：

1.    白剛玉顯微硬度20.58Gpa,維氏硬度2200-2400kg/mm2，莫氏硬度9.0。可噴砂于大部分金屬、鑄鋼件、鑄鐵件、有色金屬合金材料、含鉻含錳含鎢鉬金屬、玻璃和其他非金屬材料。

2.    白剛玉研磨能力強，噴砂效率高，由于具有很強的自銳性 ，不會對噴砂表面造成燒*氧化。

3.    白鋼玉還可以直接用于研磨拋光，表面處理，噴砂除銹等領域，可用于干式和濕式噴砂，表面拋毛拋光，噴涂前表面處理鈍化等領域。

4.    白鋼玉氧化鋁的純度高，主要晶相時α相的氧化鋁。雜質少，磁性物含量低，噴砂后不會產(chǎn)生化學殘留，可用于醫(yī)藥、航空、食品領域機械部件的噴砂。

 

 Feature：

1. The microhardness of white corundum is 20.58Gpa, the Vickers hardness is 2200-2400kg/mm2, and the Mohs hardness is 9.0. It can be sandblasted on most metals, steel castings, cast iron, non-ferrous alloy materials, chromium, manganese, tungsten and molybdenum metals, glass, and other non-metallic materials.

 

2. White corundum has strong grinding ability and high sandblasting efficiency. Due to its strong self sharpening property, it will not cause burning and oxidation on the sandblasted surface.

3. White steel jade can also be directly used in fields such as grinding and polishing, surface treatment, sandblasting and rust removal. It can be used in dry and wet sandblasting, surface roughening and polishing, and surface treatment passivation before spraying.

 

4. The purity of white steel jade alumina is high, and the main crystal phase is α Phase alumina. With low impurities and low magnetic content, sandblasting does not produce chemical residues and can be used for sandblasting mechanical components in the fields of medicine, aviation, and food.

 

 

物理指標：

顏色	白色
硬度	莫氏9.0
使用溫度	1900 ℃
熔點	2250 ℃
比重	3.95g/cm3
體積密度	3.6g/cm3
堆積密度	1.55-1.95 g/cm3
晶形	多棱角

 

 

化學成分：

	白剛玉粒度砂 F8-F220	白剛玉微粉 F230-F2000
AL2O3	99.53%	99.27%
SiO2	0.06%	0.14%
NA2O	0.23%	0.28%
Fe2O3	0.07%	0.06%
CaO	0.03%	0.05%

 

噴砂白鋼玉的可選型號:

粒度牌號	平均粒徑（mm）	基本粒尺寸（mm）
8#	2.460	2.000-2.360
10#	2.085	1.700-2.000
12#	1.765	1.400-1.700
14#	1.470	1.180-1.400
16#	1.230	1.100-1.180
20#	1.040	0.850-1.000
22#	0.885	0.710-0.850
24#	0.745	0.600-0.710
30#	0.625	0.500-0.600
36#	0.525	0.425-0.500
40#	0.438	0.355-0.425
46#	0.370	0.300-0.355
54#	0.310	0.250-0.300
60#	0.260	0.212-0.250
70#	0.218	0.180-0.212
80#	0.185	0.150-0.180
90#	0.154	0.125-0.150
100#	0.129	0.106-0.125
120#	0.109	0.090-0.106
150#	0.082	0.063-0.075
180#	0.069	0.053-0.075
220#	0.058	0.045-0.063

 

 

JIS粒度	D0值(um)	D3值(um)	D50值(um)	D94值(um)
240#	≤ 127	≤ 103	57.0±3.0	≥ 40
280#	≤ 112	≤ 87	48.0±3.0	≥ 33
320#	≤ 98	≤ 74	40.0±2.5	≥ 27
360#	≤ 86	≤ 66	35.0±2.0	≥ 23
400#	≤ 75	≤ 58	30.0±2.0	≥ 20
500#	≤ 63	≤ 50	25.0±2.0	≥ 16
600#	≤ 53	≤ 41	20.0±1.5	≥ 13
700#	≤ 45	≤ 37	17.0±1.5	≥ 11
800#	≤ 38	≤ 31	14.0±1.0	≥ 9.0
1000#	≤ 32	≤ 27	11.5.±1.0	≥ 7.0
1200#	≤ 27	≤ 23	9.5±0.8	≥ 5.5
1500#	≤ 23	≤ 20	8.0±0.6	≥ 4.5
2000#	≤ 19	≤ 17	6.7±0.6	≥ 4.0
2500#	≤ 16	≤ 14	5.5±0.5	≥ 3.0
3000#	≤ 13	≤ 11	4.0±0.5	≥ 2.0
4000#	≤ 11	≤ 8.0	3.0±0.4	≥ 1.8
6000#	≤ 8.0	≤ 5.0	2.0±0.4	≥ 0.8
8000#	≤ 6.0	≤ 3.5	1.2±0.3	≥ 0.6

 

 

應用場景：

 

鋁合金、鋅合金等有色金屬噴砂鈍化。

金屬件噴砂，除銹，噴涂準備等表面處理。

彩嵌玻璃、裝飾玻璃噴砂霧化。

牙科假牙噴砂鈍化，粘接前處理。

陶瓷瓷磚等材料表面處理。

廚具炊具噴砂流水線。

木制家具、竹制物品噴砂表面處理。

不銹鋼、合金鋼、鑄鋼噴砂蝕刻。

復合材料、塑膠產(chǎn)品表面噴砂清理。

半導體、半導體封裝設備微噴砂。

Non ferrous metals such as aluminum alloys and zinc alloys are sandblasted and passivated.

 

Surface treatment such as sandblasting, rust removal, and spray coating preparation for metal parts.

Color embedded glass and decorative glass sandblasting and atomization.

Dental dentures sandblasting and passivation, pre bonding treatment.

Surface treatment of materials such as ceramic tiles.

Kitchen utensils sandblasting assembly line.

Sandblasting surface treatment for wooden furniture and bamboo items.

Stainless steel, alloy steel, and cast steel sandblasting and etching.

Surface sandblasting cleaning of composite materials and plastic products.

 

Semiconductor and semiconductor packaging equipment micro sandblasting.