伊薩OK Autrod 4043 ER4043鋁硅焊絲

盤絲直徑：0.8mm 1.2mm 1.6mm，7.26公斤/盤！                                         

 

氬弧焊絲：1.6mm 2.4mm 3.0mm 4.0mm 2.5公斤/筒！                             

 

拍法：盤絲請拍7的倍數(shù)；氬弧焊絲1公斤請拍1的倍數(shù)！5公斤請拍5的倍數(shù)！   

 

名稱：OK Autrod 4043鋁硅焊絲
 

標準：SFA/AWS A5.10  ER4043   EN ISO 18273  S Al 4043 (AlSi5)
 

說明：OK Autrod 4043是合金焊接與釬焊使用廣泛的焊絲之一，其可被歸類為普通型填料合金。硅含量可以改善流動性（熔濕作用），因而到焊工的青睞。該合金不易發(fā)生焊縫開裂，并可產(chǎn)生光亮且?guī)捉鼰o黑斑的焊縫外觀。

 

用途：用于焊接6???系列合金的焊接，裂紋敏感性比其他焊材要低。用于汽車、拖車、自行車零件的焊接。同時也是非常適用薄鋁板和管的釬焊。

OK Autrod 4043

GMAW

OK Autrod 4043 is one of the most widely used welding and brazing alloys and can be classified as a general-purpose filler alloy. The silicon addition results in improved fluidity (wetting action), making the alloy the preferred choice of welders. The alloy is not sensitive to weld cracking and produces bright, almost smut-free welds. Not recommended for anodising. Non-heat treatable.

Welding current

DC( )

Classifications Approvals Typical all weld metal composition, % Typical mech. properties all weld metal

SFA/AWS A5.10 ER4043

EN ISO 18273

S Al 4043 (AlSi5)

EN ISO 18273

S Al 4043A (AlSi5(A))

CWB AWS A5.10 (Item number ending with A)

DB 61.039.05

CE EN 13479

VdT?V 12187

Si 5,0   Mn <0,05   Cr <0,05   Cu <0,05   Ti <0,15   Zn 0,10   Fe <0,6

Wire composition

Yield stress, MPa  55

Tensile strength, MPa  165

Elongation, %  18

Elongation, %  18

 

Diameter, mm             0,8         0,9         1,0           1,2           1,6       2.0      2,4

Arc voltage, V           13-24     13-24    15-26      20-29      25-30       -      26-31

Welding current, A   60-170  60-170  90-210  140-260  190-350     -    280-400

Wire feed, m/min       5-13      5-13      7-14         6-13       4,5-7,5    -       3,5-5

Deposition rate kg weld metal/hour 

                                   0,4-1,1  0,5-1,3  0,9-1,8    1,2-2,4     1,5-2,5     -      2,5-3,7