Alloy AA6023 is developed specifically for electronics and automotive industry for machining applications and it is renowned for good machining characteristics and excellent anodizing response. Used for automotive brake components, hydraulic valve blocks and many other applications. AA6023 alloy is replacement for 6012 and 6262, where lead is replaced with tin and bismuth and retains all the technological properties of the original alloys.

1) chemische Zusammensetzung nach DIN EN 573-3 [in % der Masse, Rest Al]

%     Si     Fe     Cu     Mn    Mg   Cr Ni Zn Ti    Bi      Sn    zus
min.  0,6    -      0,20  0,20  0,40  -   -   -    -   0,30  0,6    -
max. 1,4  0,50  0,50  0,6    0,9    -   -   -    -   0,8    1,2   0,15
2) mechanische Eigenschaften nach DIN EN 754-2 gezogen / DIN EN 755-2 gepresst

Werkstoffzustand Maβe in mm      Rm MPa      Rp0,2 MPa   A%   A50mm%    HBW
                             Da     Sb       min. max.     min. max.    min.       min.       typ.Wert
    T6                  6≥80  15≥80   320   -           270   -        10            -               -
    T8                  6≥50      -        340   -            310   -         8             -               -

    T6                   ≤150  15≥80  320   -            270   -        10            8              -
Da = Durchmesser von Rundstangen / Sb= Schlüsselweite von Vierkant- und Sechskantstangen, Dicke von Rechteckstangen / c Die

Eigenschaften dürfen durch Abschrecken an der Presse erzielt werden.