Alumec89鋁合金棒

Aluminum

ALUMINIO ALLOY ZINC ALUMEC-79

Application and uses 
Matrices: For injection 
Molds: For plastic injection
Molds: For rubber injected, shoes and boots.
Molds: For injected. It(He,She) skims off polyethylene, FOAM
Molds: Of embutición deep. On Empty.
Molds: Blow/ made by blowing.
Support for plastic molds.
Molds: For extrusion of plastic.
Molds: robotic prototypes.

Properties
High conductive thermal. Thermal conductivity is four times superior to Steel which allows you to work more efficiently and better when it comes to producing plastics or rubber.
Automation of high precision cuts reduce time delays and has an excellent quality with its precised cuts. 
Easy to use, The weight of Aluminum is 61% inferior to Steel or 1/3 of its weight which facilitates the manipulation of the metal. 
Stable Dimensions, during the production there are two states which are the framework and a strecthed position, which assures the most complete and stable dimension. 

Resistance to Corrosion: it´s resistant to all plastics and that is why there is no need to place a crome or nikel finish, even though it is allowed. 
SOLDERING has a good attribute which can be soldered to the sistemas of TIG and MIG. 
ELECTRO GALVANIZACIÓN It can be crome, nikel and can be gold plated to resist 高標(biāo)準(zhǔn) damage from Sodium Chloride. 
ADONIZADO I LAST the ALUMEC-79 Can be hardened superficially by means of this operation, reaching a superficial hardness of 65 Re. 
Application: the resistances of ALUMEC-79 coibutes to an increase in life span of the utility of the molds. Thanks to the mechanical characteristics it can be utilized for example: for the same plates of thickness of steel. when creating Aluminum, you must not forget the felixibility of Aluminum, which is three times superior to steel which is aproximated at. 70 KN/mm2 (front aprox. 210 KN/mm2, for steel) at a good temperature. For this reason we must analyze and apply Inertia in the different types of metal plates to limit the effects of the arrows.For this reason it is necessary to analyze and come the case to increase for every case of application.COUPLE(PAR) OF INERTIA of the different plates, to limit the effects of the arrow that can manage to be necessary to use plate that presents a COUPLE OF INERTIA three times mas raised. With everything, the saving weight will be of the order of 50 %.

 

Chemical Properties

%	Si	Fe	Cu	Mn	Mg	Cr	Zn	Ti		Other	Al
Min.Max	0,40	0,50	0,70	0,30	2,60	0,18 0,28	4,30	0,20	Zr + Ti 0,25	0,15	Resto

 

International Equivalencies

USA	SPAIN			FRANCE	GERMANY	G.B	SWEEDEN	SWITZERLAND	CANADA	ITALY
A.A.		U.N.E.		AFNOR	DIN(1712-1725)	B.S.	S.I.S.	VSM	ALCAN	UNI

 

Mechanical Properties

STATE	Breaking Point  Rm N/mm2	Elasticity Limit  Rp 0.2 N/mm2	Length 5,65 V So	Resistance of the Cizalladura N/mm2	Life Span
					Brinell(HB)	Vickers
T6	450 - 520	390 - 450	10	340	150

 

Fisical Properties

Elastic Model  N/mm2	Specific Weight  gms/cm3	Temperature of Fusion  ºC	Coefficient of dilatac. linear (20º-100º) 10-6/ºC	Thermal Conductive w/m ºC	Electrical Resistance Micro Ohm cm.	Electrical Conductive % IACS	Potential of dissolution V.
72.000	2,8	475-630	23,5	130	5,2	34	-

 

 

Alloy of aluminium alumec-79 measurements of normalized plates

Thickness m/m	Size m/m	Size m/m	Thickness m/m
10	1250 x 2500	100	1500 x 3000
12	1250 x 2500	110	1500 x 3000
15	1250 x 2500	120	1500 x 3000
20	1500 x 3000	130	1500 x 3000
25	1250 x 2500	150	1500 x 3000
30	1500 x 3000	180	1500 x 3000
40	1250 x 2500	200	1500 x 3000
50	1500 x 3000	225	1500 x 3000
60	1500 x 3000	250	1500 x 3000
70	1500 x 3000	300	1500 x 3000
80	1500 x 3000	-	-
90	1500 x 3000	-	-